Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_103_3_3768140_K9F4iW.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 17.11 T-atoms per nm^3
Material density = 1.707 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6141 Angstrom
T1  -- O1  = 1.6160 Angstrom
T1  -- O2  = 1.6297 Angstrom
T1  -- O3  = 1.6254 Angstrom
      mean = 1.6213 Angstrom
        t1 = 0.009234  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004330  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6245 Angstrom
T2  -- O2  = 1.6266 Angstrom
T2  -- O4  = 1.6221 Angstrom
T2  -- O5  = 1.6250 Angstrom
      mean = 1.6245 Angstrom
        t1 = 0.010152  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004753  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6251 Angstrom
T3  -- O5  = 1.6245 Angstrom
T3  -- O6  = 1.6222 Angstrom
T3  -- O6  = 1.6226 Angstrom
      mean = 1.6236 Angstrom
        t1 = 0.009386  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004102  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6141 A <--> 1.6297 A
          Mean   = 1.6231 A
          StdDev = 0.0042 A

       t1 Range  = 0.0092 <-- 0.0096 --> 0.0102
       t2 Range  = 0.0041 <-- 0.0044 --> 0.0048

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.165 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.946 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.314 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.611 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.719 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.075 deg; O2  -- O3  = 3 A
       108.165 deg <-- 109.472 deg --> 110.719 deg

O4  -- T2  -- O2  = 108.905 deg; O4  -- O2  = 3 A
O4  -- T2  -- O4  = 110.546 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.844 deg; O4  -- O5  = 3 A
O2  -- T2  -- O4  = 110.228 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 108.137 deg; O2  -- O5  = 3 A
O4  -- T2  -- O5  = 109.144 deg; O4  -- O5  = 3 A
       108.137 deg <-- 109.467 deg --> 110.546 deg

O3  -- T3  -- O5  = 108.270 deg; O3  -- O5  = 3 A
O3  -- T3  -- O6  = 110.278 deg; O3  -- O6  = 3 A
O3  -- T3  -- O6  = 108.969 deg; O3  -- O6  = 3 A
O5  -- T3  -- O6  = 109.257 deg; O5  -- O6  = 3 A
O5  -- T3  -- O6  = 109.777 deg; O5  -- O6  = 3 A
O6  -- T3  -- O6  = 110.259 deg; O6  -- O6  = 3 A
       108.270 deg <-- 109.468 deg --> 110.278 deg

        O-T-O SUMMARY
          Range  = 108.1374 deg <--> 110.7186 deg
          Mean   = 109.4690 deg
          StdDev = 0.7797 deg

        O--O SUMMARY
          Range  = 2.6159 A <--> 2.6683 A
          Mean   = 2.6505 A
          StdDev = 0.0135 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O1  - T1  = 110.362 deg; T2  -- T1  = 4.8603 A
T2  - O1  - T1  - O2  - T1  = 103.284 deg; T2  -- T1  = 4.6425 A
T2  - O1  - T1  - O3  - T3  =  60.632 deg; T2  -- T3  = 2.9617 A
T1  - O1  - T1  - O2  - T1  = 114.765 deg; T1  -- T1  = 5.0533 A
T1  - O1  - T1  - O3  - T3  = 112.223 deg; T1  -- T3  = 4.9366 A
T1  - O2  - T1  - O3  - T3  = 132.981 deg; T1  -- T3  = 5.4531 A

T1  - O4  - T2  - O2  - T2  = 122.433 deg; T1  -- T2  = 5.2526 A
T1  - O4  - T2  - O4  - T2  = 114.893 deg; T1  -- T2  = 5.0516 A
T1  - O4  - T2  - O5  - T3  =  60.128 deg; T1  -- T3  = 2.9469 A
T2  - O2  - T2  - O4  - T2  = 110.660 deg; T2  -- T2  = 5.0533 A
T2  - O2  - T2  - O5  - T3  = 133.813 deg; T2  -- T3  = 5.5505 A
T2  - O4  - T2  - O5  - T3  = 106.476 deg; T2  -- T3  = 4.8343 A

T1  - O3  - T3  - O5  - T2  =  59.240 deg; T1  -- T2  = 2.9203 A
T1  - O3  - T3  - O6  - T3  = 104.607 deg; T1  -- T3  = 4.7475 A
T1  - O3  - T3  - O6  - T3  = 123.400 deg; T1  -- T3  = 5.2825 A
T2  - O5  - T3  - O6  - T3  = 108.251 deg; T2  -- T3  = 4.8735 A
T2  - O5  - T3  - O6  - T3  = 136.428 deg; T2  -- T3  = 5.5846 A
T3  - O6  - T3  - O6  - T3  = 111.738 deg; T3  -- T3  = 5.0533 A

        T-T-T SUMMARY
          Range  = 59.2401 deg <--> 136.4278 deg
          Mean   = 107.0174 deg
          StdDev = 23.1909 deg

        T--T SUMMARY
          Range  = 2.9203 A <--> 5.5846 A
          Mean   = 4.7255 A
          StdDev = 0.8396 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 136.465 deg ; T1  -- T1   2.9997 A

T1  -- O2  -- T2  = 127.492 deg ; T1  -- T2   2.9203 A

T1  -- O3  -- T3  = 130.080 deg ; T1  -- T3   2.9469 A

T2  -- O4  -- T2  = 142.263 deg ; T2  -- T2   3.0721 A

T2  -- O5  -- T3  = 131.402 deg ; T2  -- T3   2.9617 A

T3  -- O6  -- T3  = 140.340 deg ; T3  -- T3   3.0524 A


        T-O-T SUMMARY
          Range  = 127.4924° <--> 142.2630 deg
          Mean   = 134.6736 deg
          StdDev = 5.4778 deg

        T--T SUMMARY
          Range  = 2.9203 A <--> 3.0721 A
          Mean   = 2.9922 A
          StdDev = 0.0557 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 31 48 72 102 133 164 190 236 293 345 408 453 489
TD10 = 775
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 31 48 72 102 133 164 190 236 293 345 408 453 489
TD10 = 775
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T3 (Si): multiplicity = 8
Coordination Sequence =
    1 4 10 20 34 49 66 101 136 164 202 238 276 344 406 452 514
TD10 = 787
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

<TD10> = 779.000
Average ring size = 5.2500