Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_103_3_3666117_TvSC2j.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 29.51 T-atoms per nm^3
Material density = 2.944 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.6892 Angstrom
T1  -- O3  = 1.6429 Angstrom
T1  -- O1  = 1.7097 Angstrom
T1  -- O1  = 1.7295 Angstrom
      mean = 1.6928 Angstrom
        t1 = 0.077551  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.048036  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.7098 Angstrom
T2  -- O5  = 1.6743 Angstrom
T2  -- O6  = 1.6401 Angstrom
T2  -- O4  = 1.4906 Angstrom
      mean = 1.6287 Angstrom
        t1 = 0.089333  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.088610  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6216 Angstrom
T3  -- O5  = 1.6543 Angstrom
T3  -- O6  = 2.0388 Angstrom
T3  -- O4  = 1.5513 Angstrom
T3  -- O6  = 1.6329 Angstrom
      mean = 1.6998 Angstrom

        T-O SUMMARY
          Range  = 1.4906 A <--> 2.0388 A
          Mean   = 1.6758 A
          StdDev = 0.1229 A

       t1 Range  = 0.0776 <-- 0.0556 --> 0.0893
       t2 Range  = 0.0480 <-- 0.0455 --> 0.0886

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 102.159 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 100.902 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 113.793 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 100.756 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 113.457 deg; O3  -- O1  = 3 A
O1  -- T1  -- O1  = 122.963 deg; O1  -- O1  = 3 A
       100.756 deg <-- 109.005 deg --> 122.963 deg

O2  -- T2  -- O5  = 115.750 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 121.870 deg; O2  -- O6  = 3 A
O2  -- T2  -- O4  =  98.418 deg; O2  -- O4  = 2 A
O5  -- T2  -- O6  = 113.055 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.648 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  =  93.152 deg; O6  -- O4  = 2 A
       93.152 deg <-- 108.649 deg --> 121.870 deg

O3  -- T3  -- O5  = 119.755 deg; O3  -- O5  = 3 A
O3  -- T3  -- O6  =  96.250 deg; O3  -- O6  = 3 A
O3  -- T3  -- O4  = 116.827 deg; O3  -- O4  = 3 A
O3  -- T3  -- O6  =  85.633 deg; O3  -- O6  = 2 A
O5  -- T3  -- O6  =  89.393 deg; O5  -- O6  = 3 A
O5  -- T3  -- O4  = 122.886 deg; O5  -- O4  = 3 A
O5  -- T3  -- O6  =  80.132 deg; O5  -- O6  = 2 A
O6  -- T3  -- O4  =  77.377 deg; O6  -- O4  = 2 A
O6  -- T3  -- O6  = 168.791 deg; O6  -- O6  = 4 A
O4  -- T3  -- O6  = 111.668 deg; O4  -- O6  = 3 A
       77.377 deg <-- 106.871 deg --> 168.791 deg

        O-T-O SUMMARY
          Range  = 77.3772 deg <--> 168.7908 deg
          Mean   = 107.9380 deg
          StdDev = 18.9588 deg

        O--O SUMMARY
          Range  = 2.1160 A <--> 3.6544 A
          Mean   = 2.6796 A
          StdDev = 0.3194 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 151.093 deg ; T1  -- T1   3.3304 A

T1  -- O2  -- T2  = 130.572 deg ; T1  -- T2   3.0877 A

T1  -- O3  -- T3  = 125.238 deg ; T1  -- T3   2.8988 A

T2  -- O4  -- T3  =  98.979 deg ; T2  -- T3   2.3130 A

T2  -- O5  -- T3  = 114.486 deg ; T2  -- T3   2.7993 A

T2  -- O6  -- T3  =  77.070 deg ; T2  -- T3   2.3130 A
T2  -- O6  -- T3  = 159.763 deg ; T2  -- T3   3.2222 A
T3  -- O6  -- T3  = 107.807 deg ; T3  -- T3   2.9764 A


        T-O-T SUMMARY
          Range  = 77.0703° <--> 159.7628 deg
          Mean   = 120.6259 deg
          StdDev = 25.5674 deg

        T--T SUMMARY
          Range  = 2.3130 A <--> 3.3304 A
          Mean   = 2.8676 A
          StdDev = 0.3601 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O6  = 2.2120 A
O4  -- O6  = 2.2761 A
O5  -- O6  = 2.1160 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.0877 Angstrom
  T2  -- T2  = 3.0257 Angstrom
  T2  -- T3  = 2.3130 Angstrom
  T2  -- T3  = 2.7993 Angstrom
  T2  -- T3  = 3.2222 Angstrom
  T2  -- T2  = 3.0257 Angstrom
T3  has 6 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T3  -- T1  = 2.8988 Angstrom
  T3  -- T2  = 2.3130 Angstrom
  T3  -- T2  = 2.7993 Angstrom
  T3  -- T3  = 2.9764 Angstrom
  T3  -- T2  = 3.2222 Angstrom
  T3  -- T3  = 2.9764 Angstrom